Ultrahigh Carrier Mobilities in Ferroelectric Domain Wall Corbino Cones at Room Temperature.

Recently, electrically conducting heterointerfaces between dissimilar band insulators (such as lanthanum aluminate and strontium titanate) have attracted considerable research interest. Charge transport and fundamental aspects of conduction have been thoroughly explored. Perhaps surprisingly, similar studies on conceptually much simpler conducting homointerfaces, such as domain walls, are not nearly so well developed. Addressing this disparity, magnetoresistance is herein reported in approximately conical 180° charged domain walls, in partially switched ferroelectric thin-film single-crystal lithium niobate. This system is ideal for such measurements: first, the conductivity difference between domains and domain walls is unusually large (a factor of 1013 ) and hence currents driven through the thin film, between planar top and bottom electrodes, are overwhelmingly channeled along the walls; second, when electrical contact is made to the top and bottom of the domain walls and a magnetic field is applied along their cone axes, then the test geometry mirrors that of a Corbino disk: a textbook arrangement for geometric magnetoresistance measurement. Data imply carriers with extremely high room-temperature Hall mobilities of up to ≈3700 cm2 V-1 s-1 . This is an unparalleled value for oxide interfaces (and for bulk oxides) comparable to mobilities in other systems seen at cryogenic, rather than at room, temperature.

An Electronically Driven Improper Ferroelectric: Tungsten Bronzes as Microstructural Analogs for the Hexagonal Manganites.

Since the observation that the properties of ferroic domain walls (DWs) can differ significantly from the bulk materials in which they are formed, it has been realized that domain wall engineering offers exciting new opportunities for nanoelectronics and nanodevice architectures. Here, a novel improper ferroelectric, CsNbW2 O9 , with the hexagonal tungsten bronze structure, is reported. Powder neutron diffraction and symmetry mode analysis indicate that the improper transition (TC = 1100 K) involves unit cell tripling, reminiscent of the hexagonal rare earth manganites. However, in contrast to the manganites, the symmetry breaking in CsNbW2 O9 is electronically driven (i.e., purely displacive) via the second-order Jahn-Teller effect in contrast to the geometrically driven tilt mechanism of the manganites. Nevertheless CsNbW2 O9 displays the same kinds of domain microstructure as those found in the manganites, such as the characteristic six-domain "cloverleaf" vertices and DW sections with polar discontinuities. The discovery of a completely new material system, with domain patterns already known to generate interesting functionality in the manganites, is important for the emerging field of DW nanoelectronics.

Large Carrier Mobilities in ErMnO3 Conducting Domain Walls Revealed by Quantitative Hall-Effect Measurements.

Kelvin probe force microscopy (KPFM) has been used to directly and quantitatively measure Hall voltages, developed at conducting tail-to-tail domain walls in ErMnO3 single crystals, when current is driven in the presence of an approximately perpendicular magnetic field. Measurements across a number of walls, taken using two different atomic force microscope platforms, consistently suggest that the active p-type carriers have unusually large room temperature mobilities of the order of hundreds of square centimeters per volt second. Associated carrier densities were estimated to be of the order of 1013 cm-3. Such mobilities, at room temperature, are high in comparison with both bulk oxide conductors and LaAlO3-SrTiO3 sheet conductors. High carrier mobilities are encouraging for the future of domain-wall nanoelectronics and, significantly, also suggest the feasibility of meaningful investigations into dimensional confinement effects in these novel domain-wall systems.